Raise3D Industrial PA12 CF+ is a carbon fiber-reinforced composite filament based on Polyamide 612 (PA612, Nylon 612). PA612 inherits the best characteristics of both PA6 and PA12, such as toughness and reduced water absorption. By adding 15 wt.% short carbon fibers with optimized length distribution, mechanical, thermal properties and even surface quality of printed parts are all enhanced.

Compared with Raise3D Industrial PA12 CF, it exhibits higher strength-to-weight ratio, better interlayer bonding quality (Z-direction strength) and better dimensional stability. After annealing, thermal and mechanical properties are improved further. PA12CF+ is an optimal choice for lightweight and strong end-use applications, such as jigs, fixtures, and many other functional parts in the fields of manufacturing, automotive, and aerospace.

Properties

• Superior interlayer bonding strength
• Stiff and strong
• High strength-to-weight ratio
• Lower shrinkage ratio
• Heat and wear resistant
• Chemical resistant

Applications

• Manufacturing
• Automotive
• Aerospace
• Jigs & Fixtures

Compatibility
This filament is compatible with Raise3D Industrial PA12 CF Support Filament and PVA+.

Please note, carbon fiber reinforced filament is abrasive and can wear out brass nozzles quickly. It is suggested to print carbon fiber filament with hardened nozzle.

Basis 3D Print Setting                          

Extruder temp	270±300ºC
Bed temp	60˚C
Heated chamber temp	RT-120˚C
Nozzle requirements	Using an abrasion-resistant nozzle, such as hardened steel and ruby nozzle, is highly recommended.
Bed adhesion	Dimafix, Magigoo, BuildTak
Drying recommendation	Dry before printing, 70-80ºC
Support material	PA12 CF Support