BASF ULTRAFUSE® 17-4 PH 1.75mm 3kg

Art nr.210000004407
Ultrafuse® 17-4 PH is a filament for the production of metal components in 17-4 stainless steel on standard Fused Filament Fabrication (FFF) printers. This stainless steel can be fully heat treated to high levels of strength and hardness. It is therefore ideal for Petrochemistry, Aerospace, the Auto
Prijs €297
prijs per Piece
excl. BTW
2 op voorraad
Piece

Omschrijving

Ultrafuse® 17-4 PH is a filament for the production of metal components in 17-4 stainless steel on standard Fused Filament Fabrication (FFF) printers. This stainless steel can be fully heat treated to high levels of strength and hardness. It is therefore ideal for Petrochemistry, Aerospace, the Automotive and the Medical Industry. Parts printed with our metal-polymer composite filament Ultrafuse® 17-4 PH obtain their final properties through a catalytic debinding and sintering process known from traditional Metal Injection Molding.

Benefits at a Glance 
- Easy and affordable way of metal 3D printing
- High mechanical strength and hardness
- Good corrosion resistance
- Fully hardened enables highest strength
- Wide range of post-processing options for green parts

Specificaties

Merk
BASF
GTIN
8718969926331
Article no. manufacturer
UMF-5033s300
Filament diameter
1.75mm
Density
0 g/cc
Tensile strength
880 MPa
Tensile modulus
0 MPa
Elongation at break
6 %
Flexural strength
0 MPa
Flexural modules
0 MPa
Izod impact (notched)
0 J/m

BASF ULTRAFUSE® 17-4 PH 1.75mm 3kg

Art nr.210000004407
Ultrafuse® 17-4 PH is a filament for the production of metal components in 17-4 stainless steel on standard Fused Filament Fabrication (FFF) printers. This stainless steel can be fully heat treated to high levels of strength and hardness. It is therefore ideal for Petrochemistry, Aerospace, the Auto
Prijs €297
prijs per Piece
excl. BTW
2 op voorraad
Piece

Omschrijving

Ultrafuse® 17-4 PH is a filament for the production of metal components in 17-4 stainless steel on standard Fused Filament Fabrication (FFF) printers. This stainless steel can be fully heat treated to high levels of strength and hardness. It is therefore ideal for Petrochemistry, Aerospace, the Automotive and the Medical Industry. Parts printed with our metal-polymer composite filament Ultrafuse® 17-4 PH obtain their final properties through a catalytic debinding and sintering process known from traditional Metal Injection Molding.

Benefits at a Glance 
- Easy and affordable way of metal 3D printing
- High mechanical strength and hardness
- Good corrosion resistance
- Fully hardened enables highest strength
- Wide range of post-processing options for green parts

Specificaties

Merk
BASF
GTIN
8718969926331
Article no. manufacturer
UMF-5033s300
Filament diameter
1.75mm
Density
0 g/cc
Tensile strength
880 MPa
Tensile modulus
0 MPa
Elongation at break
6 %
Flexural strength
0 MPa
Flexural modules
0 MPa
Izod impact (notched)
0 J/m