MakerPoint PLA filament is a tough, easy to use high-grade PLA ideal for 3D printing. Our unique material compound makes is tougher and less brittle than standard PLA 3D-printing filaments. Due to a low shrinkage factor, MakerPoint PLA will not deform after cooling. PLA (Poly Lactic Acid) is a biodegradable plastic made from renewable natural resources and one of the most popular materials for 3D printing.
Features
- Tougher and less brittle compared to regular PLA
- Easy to print at low temperature
- Low warping
- Biodegradable
- Limited smell
Dimensions
|
|
|
| Size |
tolerance |
Roundness |
| 1,75mm |
± 0,05mm |
95% |
| 2,85mm |
± 0,10mm |
95% |
Colors
|
|
|
| MakerPoint PLA is available in a large selection of bright colors. Special colors are available upon request with a minimum order quantity of 20kg. |
3D-printing
|
|
|
| Description |
|
Typical value |
| Printing technology |
|
FFF |
| Printing temp. |
|
180-220˚C |
| Heated bed temp. |
|
± 35-60˚C (when available) |
| Cooling fan |
|
100% |
| Flow Rate |
|
100% |
Physical properties
|
| Description |
Test method |
Typical value |
| Specific gravity |
ISO 1183 |
1,24 g/cc |
| MFR 210°C/2,16 kg |
ISO 1133 |
9,56 gr/10 min |
| Yield stress |
ISO 527 |
69,8 MPa |
| Strain at break |
ISO 527 |
19,5% |
| E-modulus |
ISO 527 |
3120 MPa |
Impact Strength -
Charpy method 23˚C |
ISO 179 |
3,4 KJ/m² |
| Moisture absorption |
ISO 62 |
1968 ppm |
Thermal properties
|
| Description |
Test method |
Typical value |
| Melting temp. |
ISO 11357 |
77-146˚C |
| Vicat softening temp. |
ISO 306 |
60˚C |
| Glass transaction temp. |
ISO 11357 |
57˚C |